应力腐蚀的标准有哪些?(收藏目录)
2025-07-07 13:51:00 作者:薛俊鹏 来源:考拉腐蚀 分享至:

 汇总了常用的国标、行标、团标中应力腐蚀实验方法标准,分享如下:

1、GB/T 15970.1-2018 金属和合金的腐蚀 应力腐蚀试验 第1部分:试验方法总则 Corrosion of metals and alloys—Stress corrosion testing—Part 1:General guidance on testing procedures
2、GB/T 15970.2-2000 金属和合金的腐蚀 应力腐蚀试验 第2部分:弯梁试样的制备和应用 Corrosion of metals and alloys--Stress corrosion testing--Part 2:Preparation and use of bent-beam speciments

 

3、GB/T 15970.3-1995 金属和合金的腐蚀 应力腐蚀试验 第3部分:U型弯曲试样的制备和应用 Corrosion of metals and alloys-Stress corrosion testing-Part 3: Preparation and use of U-bend specimens

4、GB/T 15970.4-2000 金属和合金的腐蚀 应力腐蚀试验 第4部分:单轴加载拉伸试样的制备和应用 Corrosion of metals and alloys-Stress corrosion testing-Part 4:Preparation and use of uniaxially loaded tension specimens

5、GB/T 15970.5-1998 金属和合金的腐蚀 应力腐蚀试验 第5部分:C型环试样的制备和应用 Corrosion of metals and alloy—Stress corrosion testing—Part 5:Preparation and use of C-ring specimens

6、GB/T 15970.6-2007 金属和合金的腐蚀 应力腐蚀试验 第6部分:恒载荷或恒位移下的预裂纹试样的制备和应用 Corrosion of metals and alloys—Stress corrosion testing—Part 6:Preparation and use of pre-cracked specimens for tests under constant load or constant displacement

7、GB/T 15970.7-2017 金属和合金的腐蚀 应力腐蚀试验 第7部分: 慢应变速率试验 Corrosion of metals and alloys—Stress corrosion testing—Part 7:Slow strain rate testing

8、GB/T 15970.8-2005 金属和合金的腐蚀 应力腐蚀试验 第8部分 焊接试样的制备和应用 Corrosion of metals and alloys—Stress corrosion test—Part 8:Preparation and use of speciments to evaluate weldments

9、 GB/T 15970.9-2007 金属和合金的腐蚀 应力腐蚀试验 第9部分:渐增式载荷或渐增式位移下的预裂纹试样的制备和应用 Corrosion of metals and alloys—Stress corrosion testing—Part 9:Preparation and use of pre-cracked speciments for tests under rising load or rising displacement

10、GB/T 15970.10-2021 金属和合金的腐蚀 应力腐蚀试验 第10部分:反向U型弯曲试验方法 Corrosion of metals and alloys—Stress corrosion testing—Part 10:Reverse U-bend method

 

 

实验设备-高温、高压、应力腐蚀

11、GB/T 15970.11-2022 金属和合金的腐蚀 应力腐蚀试验 第11部分:金属和合金氢脆和氢致开裂试验指南 Corrosion of metals and alloys—Stress corrosion cracking—Part 11:Guidelines for testing the resistance of metals and alloys to hydrogen embrittlement and hydrogen-assisted cracking 

12、GB/T 15972.33-2024 光纤试验方法规范 第33部分:机械性能的测量方法和试验程序 应力腐蚀敏感性参数 Specifications for optical fibre test methods—Part 33:Measurement methods and test procedures for mechanical characteristics— Stress corrosion susceptibility 

13、GB/T 20122-2006 金属和合金的腐蚀 滴落蒸发试验的应力腐蚀开裂评价 Corrosion of metals and alloys—Evaluation of stress corrosion cracking by the drop evaporation test

14、GB/T 22640-2023 铝合金应力腐蚀敏感性评价试验方法 Test method for determining susceptibility to stress corrosion cracking of aluminium alloys

15、GB/T 24518-2009 金属和合金的腐蚀 应力腐蚀室外暴露试验方法 Corrosion of metals and alloys—Test methods for stress corrosion cracking in outdoor environments

16、 GB/T 25996-2019 绝热材料对奥氏体不锈钢外部应力腐蚀开裂的试验方法 Test method for thermal insulations on external stress corrosion cracking of austenitic stainless steel

17、GB/T 33883-2017 7XXX系铝合金应力腐蚀试验 沸腾氯化钠溶液法 Test methods for stress corrosion of 7××× series aluminum alloys—Boiling sodium chloride solution method

18、GB/T 36676-2018 埋地钢质管道应力腐蚀开裂(SCC)外检测方法 External inspection methodology of stress corrosion cracking(SCC)forburied steel pipelines

19、GB/T 40339-2021 金属和合金的腐蚀 服役中检出的应力腐蚀裂纹的重要性评估导则 Corrosion of metals and alloys—Guidelines for assessing the significances of stress corrosion cracks detected in service

20、 GB/T 40403-2021 金属和合金的腐蚀 用四点弯曲法测定金属抗应力腐蚀开裂的方法 Corrosion of metals and alloys—Methodology for determining the resistance of metals to stress corrosion cracking using the four-point bend method 

 

硫化氢腐蚀实验室设施及设备

21、GB/T 4157-2017 金属在硫化氢环境中抗硫化物应力开裂和应力腐蚀开裂的实验室试验方法 Laboratory testing of metals for resistance to sulfide stress crackingand stress corrosion cracking in H2S environment

22、 GB/T 42661-2023 金属和合金的腐蚀 模拟海洋环境中钢筋应力腐蚀敏感性试验方法  Corrosion of metals and alloys—Test method for determining susceptibility to stress corrosion of steel reinforcement in simulated marine environment

23、 GB/T 43925-2024 套管和油管全尺寸拉伸应力腐蚀试验方法 Test method for full-scale tensile stress corrosion testing of casing and tubing

24、 MH/T 6072-2019 飞机发动机清洗用化学品对钛合金应力腐蚀的试验方法 

25、SY/T 0599-2018 天然气地面设施抗硫化物应力开裂和应力腐蚀开裂金属材料技术规范

26、SY/T 7348-2016 钢质管道及储罐腐蚀评价标准 第 4部分: 埋地钢质管道应力腐蚀开裂直接评价 NACE RP0204-2004,MOD

27、T/CAPEC 46-2024 金属在硫化氢环境中抗硫化物应力开裂和应力腐蚀开裂试验监理技术要求 Supervision technical requirements for testing of metals for resistance to sulfide stress cracking and stress corrosion cracking in H2S environment

28、T/CCTAS 55-2023  轨道交通车辆用抗应力腐蚀铝合金材料过程控制要求 Preparation process requirements for stress corrosion control of aluminum alloy materials used in rail transit vehicles

29、T/CNS 13-2019 核电厂金属材料高温高压水中模拟辐照促进应力腐蚀开裂敏感性试验方法 Test method for simulated-irradiation assisted stress corrosion cracking susceptibility in high temperature pressurized water of metallic materials for nuclear power plants

30、 T/CNS 5-2018 核电厂金属材料高温高压水中应力腐蚀裂纹扩展试验方法 Test method for stress corrosion crack growth in high temperature pressurized water of metallic materials for nuclear power plants 

 

 

常见应力腐蚀标准试验方法对比及应用

31、YB/T 5344-2006 铁-铬-镍合金在高温水中应力腐蚀试验方法 Fe-Cr-Ni alloys-stress corrosion test in high temperature water

32、YB/T 5362-2006 不锈钢在沸腾氯化镁溶液中应力腐蚀试验方法 Test method for stress corrosion-cracking resistance of stainless steels in a boiling magnesium chloride solution 

33、YS/T 814-2012 黄铜制成品应力腐蚀试验方法 Test method for stress corrosion resistance of brass finished products 

34、GB/T 45879-2025 金属和合金的腐蚀 应力腐蚀敏感性电化学快速试验方法 Corrosion of metals and alloys-Electrochemical methods for fast test of stress corrosion cracking susceptibility

几种应力腐蚀试样实物图如下,依次是U型弯曲、三点弯曲、四点弯曲、C型环试样;

 

 

免责声明:本网站所转载的文字、图片与视频资料版权归原创作者所有,如果涉及侵权,请第一时间联系本网删除。