摘要
针对3A21铝合金在乙二醇冷却液中的腐蚀问题,采用浸泡实验和表面分析技术系统研究了痕量Cl-和Cu2+对3A21铝合金在50 ℃乙二醇-水冷却液中腐蚀行为的影响。结果表明,Cl-引发了铝合金的点腐蚀,随着Cl-浓度增大,铝合金点蚀敏感性增大。Cu2+促进铝合金钝化膜的破裂,并与Al发生置换反应沉积在铝合金表面,电偶作用加速了铝合金的腐蚀。Cl-和Cu2+共存时,钝化膜破裂和电偶作用导致铝合金腐蚀加剧。
关键词: 3A21铝合金 ; 乙二醇 ; 痕量离子 ; 点蚀
Abstract
In view of the corrosion of 3A21 Al-alloy in glycol coolant, this paper studied the influence of trace amounts of Cl- and Cu2+ ions on the corrosion behavior of 3A21 Al-alloy in ethylene glycol-water coolant at 50 ℃ by immersion experiments and surface analysis technology. The results indicated that Cl- ions resulted in pitting corrosion of the alloy, and the pitting corrosion susceptibility increased with the increase of the concentration of Cl-. Cu2+ ions could promote the breakdown of the passive film, and react with Al resulting in a deposition of metallic Cu on the Al-alloy surface, which in turn accelerated the corrosion of Al-alloy owing to the galvanic effect. 3A21 Al-alloy took place serious corrosion owing to the overlapping effect of the breakdown of the passive film and the galvanic effect in the case of co-existence of Cl- and Cu2+.
Keywords: 3A21 Al-alloy ; ethylene glycol ; trace ions ; pitting
免责声明:本网站所转载的文字、图片与视频资料版权归原创作者所有,如果涉及侵权,请第一时间联系本网删除。
相关文章
官方微信
《中国腐蚀与防护网电子期刊》征订启事
- 投稿联系:编辑部
- 电话:010-62316606-806
- 邮箱:fsfhzy666@163.com
- 中国腐蚀与防护网官方QQ群:140808414
点击排行
PPT新闻
“海洋金属”——钛合金在舰船的
点击数:7130
腐蚀与“海上丝绸之路”
点击数:5741